Investigating the Properties of Electrodeposited of Ni-P-ZrC Nanocomposite Coatings

Superior corrosion resistance along with higher mechanical performance is becoming a primary requirement to decrease operational costs in the industries. Nickel-based phosphorus coatings have been reported to show better corrosion resistance properties but suffer from a lack of mechanical strength. Zirconium carbide nanoparticles (ZCNPs) are known for promising hardness and unreactive behavior among variously reported reinforcements. The present study focuses on the synthesis and characterization of novel Ni-P-ZrC nanocomposite coatings developed through the electrodeposition technique. Successful coelectrodeposition of ZCNPs without any observable defects was carried out utilizing a modified Watts bath and optimized conditions. For a clear comparison, structural, surface, mechanical, and electrochemical behaviors of Ni-P and Ni-P-ZrC nanocomposite coatings containing 0.75 g/L ZCNPs were thoroughly investigated. The addition of ZCNPs has a considerable impact on the properties of Ni-P coatings. Enhancement in the mechanical properties (microhardness, nanoindentation, wear, and erosion) is observed due to reinforcement of ZCNPs in the Ni-P matrix, which can be attributed to mainly the dispersion hardening effect. Furthermore, corrosion protection efficiency (PE%) of the Ni-P matrix was enhanced by the incorporation of ZCNPs from 71 to 85.4%. The Ni-P-ZrC nanocomposite coatings provide an exciting option for their utilization in the automotive, electronics, aerospace, oil, and gas industry.

Other Information

Published in: ACS Omega
License: https://creativecommons.org/licenses/by/4.0/
See article on publisher's website: https://dx.doi.org/10.1021/acsomega.1c03117