Electrochemical studies of a high voltage Na4Co3(PO4)2P2O7–MWCNT composite through a selected stable electrolyte

journal contribution
submitted on 2024-05-27, 06:48 and posted on 2024-05-27, 06:51 authored by P. Ramesh Kumar, R. Essehli, H. B. Yahia, R Amin, I. Belharouak

Cathode materials that operate at high voltages are required to realize the commercialization of high-energy-density sodium-ion batteries. In this study, we prepared different composites of sodium cobalt mixed-phosphate with multiwalled carbon nanotubes (Na4Co3(PO4)2P2O7–MWCNTs) by the sol–gel synthesis technique. The crystal structure and microstructure were characterized by using PXRD, TGA, Raman spectroscopy, SEM and TEM. The electrochemical properties of the Na4Co3(PO4)2P2O7–20 wt% MWCNT composite were explored using two different electrolytes. The composite electrode exhibited excellent cyclability and rate capabilities with the electrolyte composed of 1 M sodium hexafluorophosphate in ethylene carbonate:dimethyl carbonate (EC:DMC). The composite electrode delivered stable discharge capacities of 80 mA h g−1 and 78 mA h g−1 at room and elevated (55 °C) temperatures, respectively. The average discharge voltage was around 4.45 V versus Na+/Na, which corresponded to the Co2+/3+ redox couple. The feasibility of the Na4Co3(PO4)2P2O7 cathode for sodium-ion batteries has been confirmed in real time using a full cell configuration vs. NaTi2(PO4)3–20 wt% MWCNT, and it delivers an initial discharge capacity of 78 mA h g−1 at 0.2C rate.

Other Information

Published in: RSC Advances
License: http://creativecommons.org/licenses/by/3.0/
See article on publisher's website: http://dx.doi.org/10.1039/d0ra02349c

History

Language

  • English

Publisher

Royal Society of Chemistry

Publication Year

  • 2020

License statement

This Item is licensed under the Creative Commons Attribution 3.0 International License.

Institution affiliated with

  • Hamad Bin Khalifa University
  • Qatar Environment and Energy Research Institute - HBKU